| PROPERTY | UNIT | VALUE / RANGE Dry (50%RH) |
| Melting Point | °C | 218 - 263 |
| Density | g mL-1 | 1.04 - 1.18 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 9 - 16.1 |
| Heat Deflection Temperature, 0.5 MPa | °C | 75 - 208 |
| Heat Deflection Temperature, 1.8 MPa | °C | 45 - ? |
| Thermal Conductivity | W / mK | 0.17 - 0.29 |
| Shore Hardness, R & M Scale | n/a | R70 - R121 (M57 - M108) |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 55 - 86 (30 - 55) |
| Tensile Strength, Break at 23 C | MPa | |
| Elongation, Yield | % | 4 - 6 (24 - 38) |
| Elongation, Break | % | 28 - 90 (50 - 100) |
| Tensile Modulus at 23 C | MPa | 2000 - 3000 (400 - 1550) |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | |
| Compressive Strength | MPa | 8 - 100 |
| Izod Notched | J / m | 4 - 90 (8 - 130) |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 2.6 - 3.9 (3.9) | |
| Dielectric Constant @ 1 MHz | n/a | 2.9 - 4.6 (3.6 - 3.7) | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 140 - 1000 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 225 - 300 | |
| Linear Mold Shrinkage | cm/cm | 0.007 - 0.018 | |
| Continuous Service Temperature | °C | 80 - 116 | |
| Water Absorption, 24 hr. Immersion | % | 6.4 - 8.5 |